The discovery of high-temperature conventional superconductivity in H3S with a critical temperature of Tc=203 K was followed by the recent record of Tc ~250 K in the face-centered cubic (fcc) lanthanum hydride LaH10 compound. It was realized in a new class of hydrogen-dominated compounds having a clathrate-like crystal structure in which hydrogen atoms form a 3D framework and surround a host atom of rare earth elements. Yttrium hydrides are predicted to have even higher Tc exceeding room temperature. In this paper, we synthesized and refined the crystal structure of new hydrides: YH4, YH6, and YH9 at pressures up to 237 GPa finding that YH4 crystalizes in the I4/mmm lattice, YH6 in Im-3m lattice and YH9 in P63/mmc lattice in excellent agreement with the calculations. The observed very high-temperature superconductivity is comparable to that found in fcc-LaH10: the pressure dependence of Tc for YH9 also displays a "dome like shape" with the highest Tc of 243 K at 201 GPa. We also observed a Tc of 227 K at 237 GPa for the YH6 phase. However, the measured Tcs are notably lower by ~30 K than predicted. Evidence for superconductivity includes the observation of zero electrical resistance, a decrease of Tc under an external magnetic field and an isotope effect. The theoretically predicted fcc YH10 with the promising highest Tc>300 K was not stabilized in our experiments under pressures up to 237 GPa.
We synthesized lanthanum hydride (LaHx) by laser heating of lanthanum in hydrogen atmosphere at pressure P = 170 GPa. The sample shows a superconducting step at 209 K and 170 GPa and temperature dependence of resistance. By releasing the pressure to 150 GPa, the superconducting transition temperature Tc increases to 215 K - the record Tc. This finding supports a way of achieving Tc higher than the one in H3S (203 K) in hydrides with sodalite-like structures, first proposed for CaH6 (Tc=245 K) and later for yttrium and lanthanum hydrides where higher, room temperature superconductivity is expected.
The recent discovery of high-temperature, high-pressure superconductors, such as hydrides and nickelates, has opened exciting avenues in studying high-temperature superconductivity. The primary superconducting properties of these materials are well characterized by measuring various electrical and magnetic properties, despite the challenges posed by the high-pressure environment. Experimental microscopic insight into the pairing mechanism of these superconductors is even more challenging, due to the lack of direct probes of the superconducting gap structures at high pressure conditions. Here, we have developed a planar tunnel junction technique for diamond anvil cells and present ground-breaking tunneling spectroscopy measurements at megabar pressures. We determined the superconducting gap of elemental sulfur at 160 GPa, a key constituent of the high-temperature superconductor H3S. High quality tunneling spectra indicate that β-Po phase sulfur is a type II superconductor with a single s-wave gap with a gap value 2Δ(0)=5.6meV. This technique is compatible with superconducting compounds synthesized in diamond anvil cells and provides insight into the pairing mechanism in novel superconductors under high-pressure conditions. Published by the American Physical Society 2024
'/%3e%3cuse xlink:href='%23a' transform='rotate(23.036 .093 25.536)'/%3e%3cuse xlink:href='%23a' transform='rotate(45.87 1.273 16.18)'/%3e%3cuse xlink:href='%23a' transform='rotate(69.945 .996 12.078)'/%3e%3cuse xlink:href='%23a' transform='rotate(20.66 -19.689 31.932)'/%3e%3c/svg%3e)
